Mono-dispersed cross-linked polystyrene micro-spheres
prepared by seed swelling polymerization method |
| WANG Dongsha, LIU Yanjun |
| Department of Chemical Engineering, Dalian Institute of Light Industry |
|
|
|
|
Abstract A two-step swelling procedure was adopted to synthesize mono-dispersed and highly cross-linked poly (St-divinylbenzene) particles with PSt micro-spheres (1.80 ?m in diameter). The PSt micro-spheres were prepared by a dispersion polymerization method and used as seeds. The effects of monomer concentration, ratio of ethanol to water, swelling reagents, crosslinking reagents, swelling temperature and agitation speed on particle size were investigated in detail. The morphologies and size distributions of these micro-spheres were examined by SEM and particle size analysis (PSA). The Tg of the micro-spheres was measured by DSC. The results indicate that the particles (6.20 ?m in diameter) exhibit excellent mono dispersed property and high crosslinking degree when the concentration of the swelling reagent was 25%, the concentration of the crosslinking reagents was 23%, the swelling temperature was 30°C and the stirring speed was 150 r/min.
|
|
Issue Date: 05 December 2008
|
|
| 1 |
Wang B S, Zhang Y G, He B L . Preparation of Microparticles of Narrow Distributed Diametersand Their Usage in Amino Acid Analysis Chem. J Chinese Univ, 1991, 12(4): 560 (in Chinese)
|
| 2 |
Ugelstad J, Mork P C, Schmid R, Ellinqsen T, Berqe A . Preparation and biochemicaland biomedical applications of new monosized polymer particles Polym Int, 1993, 30(2): 157–168
|
| 3 |
Zhang X Q, Wang S Improvseed polymerization––Synthesis of Monodispersedand Crosslinked Polystyrene Microspheres. Acta Polym Sin, 1991, 3(3): 333 (in Chinese)
|
| 4 |
Zhang H T, Huang J X, Jiang B B, Li X Q . Studies onKinetics of Copolymerization and Particle Size for Preparing MonodispersedCrosslinked Polystere Microspheres. ChineseJ Appl Chem, 2001, 18(9): 726 (in Chinese)
|
| 5 |
Zhang K, FU Q, Huang Y H, Zhou D H, Jiang L X . Preparation of crosslinked polystyrenemicrospheres in anisotropic conductive films. Insulating Materials, 2005, 3: 1–4 (in Chinese)
|
| 6 |
Zhang K, Lei Y, Wang Y G . Studies of the Preparation of Monodisperse PolystyreneMicrospheres and Its Influence Factors. Journal of Functional Polymers, 2002, 15(2): 189 (in Chinese)
|
| 7 |
Ma G G, Su Z G . Macromolecule Micro-spheresMaterial. Beijing: Chemical Industry Press, 2005 : 63 (in Chinese)
|
| 8 |
Lv R, Zhang H T . Synthesis of the CrosslinkedFunctional Polystyrene Microspheres in Micron-Size Monodisperse byDispersion Polymerization. Journal of FunctionalPolymers, 2003, 16(1): 54 (inChinese)
|
| 9 |
Li H, Zhang L L, Guan Y X, Huang C Y . Preparationof Micron Monodispersed Crosslinked Polystyrene Microspheres by SuspensionPolymerization in Glucose Aqueous Solution as Disperse Medium. Petrochemical Technology, 2006, 1: 70 (in Chinese)
|
| 10 |
Dean J, Wei J F . Lange's Chemistry HandbookVersion 15th. Beijing: Science Press, 2003
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|