Abstract：The association and properties of multi-block like copolymers (TP) of acrylamide (AM) and acrylic acid (AA) prepared by template copolymerization in aqueous solution were studied. The results showed that the copolymers of this type exhibited a significant structure effect compared with that of similar random copolymers (CP) obtained by copolymerization in the absence of template. Decreasing the value of pH or adding Ca2+ ion to the copolymer solution will make phase separation occur. The TEM images demonstrated that the phase separation caused by Ca2+ ion was due to the formation of extensively intermolecular cross-linking. With the increase of the pH value of copolymer solution, the changes of the solution viscosity was similar with that of homopolyacrylic acid, which originally increased and then decreased. But the increase range of template copolymer was higher than that of homopolyacrylic acid. TEM images indicated that at the maximal viscosity the copolymer obtained in the presence of template formed coiled aggregates.
出版日期: 2007-03-05
引用本文:
. Solution properties and self-association of multi-blocks like copolymer P(AM/AA) prepared by template copolymerization[J]. Frontiers of Chemical Engineering in China, 2007, 1(1): 68-71.
ZHANG Yuxi, WU Feipeng, LI Miaozhen, WANG Erjian. Solution properties and self-association of multi-blocks like copolymer P(AM/AA) prepared by template copolymerization. Front. Chem. Sci. Eng., 2007, 1(1): 68-71.