Fluorene-based narrow-band-gap copolymers for
red light-emitting diodes and bulk heterojunction photovoltaic cells |
| SUN Mingliang, WANG Li, XIA Yangjun, DU Bin, LIU Ransheng, CAO Yong |
| Institute of Polymer Optoelectronic Materials and Devices, Key Laboratory of Special Functional Materials, South China University of Technology; |
|
|
|
|
Abstract A series of narrow band-gap conjugated copolymers (PFO-DDQ) derived from 9,9-dioctylfluorene (DOF) and 2,3-dimethyl-5,8-dithien-2-yl-quinoxalines (DDQ) is prepared by the palladium-catalyzed Suzuki coupling reaction with the molar feed ratio of DDQ at around 1%, 5%, 15%, 30% and 50%, respectively. The obtained polymers are readily soluble in common organic solvents. The solutions and the thin solid films of the copolymers absorb light from 300–590 nm with two absorbance peaks at around 380 and 490 nm. The intensity of 490 nm peak increases with the increasing DDQ content in the polymers. Efficient energy transfer due to exciton trapping on narrow-band-gap DDQ sites has been observed. The PL emission consists exclusively of DDQ unit emission at around 591–643 nm depending on the DDQ content in solid film. The EL emission peaks are red-shifted from 580 nm for PFO-DDQ1 to 635 nm for PFO-DDQ50. The highest external quantum efficiency achieved with the device configuration ITO/PEDOT/PVK/PFO-DDQ15/Ba/Al is 1.33% with a luminous efficiency 1.54 cd/A. Bulk heterojunction photovoltaic cells fabricated from composite films of PFO-DDQ30 copolymer and [6,6]-phenyl C61 butyric acid methyl ester (PCBM) as electron donor and electron acceptor, respectively in device configuration: ITO/PEDOT:PSS/PFO-DDQ30:PCBM/PFPNBr/Al shows power conversion efficiencies of 1.18% with open-circuit voltage (Voc) of 0.90 V and short-circuit current density (Jsc) of 2.66 mA/cm2 under an AM1.5 solar simulator (100 mW/cm2). The photocurrent response wavelengths of the PVCs based on PFO-DDQ30/PCBM blends covers 300–700 nm. This indicates that these kinds of low band-gap polymers are promising candidates for polymeric solar cells and red light-emitting diodes.
|
|
Issue Date: 05 September 2008
|
|
| 1 |
Gustafsson G, Cao Y, Treacy G M, Klavetter F, Colaneri N, Heeger A J . Flexible light-emitting-diodes from soluble conductingpolymers. Nature, 1992, 357: 477–479.
doi:10.1038/357477a0
|
| 2 |
Heeger A J . Light emission from semiconducting polymers: light-emitting diodes,light-emitting electrochemical cells, lasers and white light for thefuture. Solid State Commun, 1998, 107: 673–679.
doi:10.1016/S0038‐1098(98)00215‐4
|
| 3 |
Hou Q, Xu Y S, Yang W, Yuan M, Peng J B, Cao Y . Novelred-emitting fluorene-based copolymers. J Mater Chem, 2002, 12: 2887–2892.
doi:10.1039/b203862e
|
| 4 |
Zhou Q M, Hou Q, Zheng L, Deng X Y, Yu G, Cao Y . Fluorene-basedlow band-gap copolymers for high performance photovoltaic devices. Appl Phys Lett, 2004, 84: 1653–1655.
doi:10.1063/1.1667614
|
| 5 |
Ma L P,Yang Y . Unique architecture and conceptfor high-performance organic transistors. Appl Phys Lett, 2004, 85: 5084–5086.
doi:10.1063/1.1821629
|
| 6 |
Ohmori Y, Uchida M, Muro K, Yoshino K . Blueelectoluminescent diodes utilizing poly(alkylfluorene). Jpn J Appl Phys, 1991, 30: 1941–1943.
doi:10.1143/JJAP.30.L1941
|
| 7 |
Pei Q B, Yang Y . Efficient photoluminescenceand electroluminescence from a soluble polyfluorene. J Am Chem Soc, 1996, 118: 7416–7417.
doi:10.1021/ja9615233
|
| 8 |
Xia Y J, Deng X Y, Wang L, Li X Z, Cao Y . Synthesis and characterization of near-infrared electroluminescentfluorene-based conjugated copolymers. ActaPolymerica Sinica, 2006, 5: 697–702 (in Chinese)
|
| 9 |
Yang R Q, Tian R Y, Yan J G, Zhang Y, Yang J, Hou Q, Yang W, Zhang C, Cao Y . Deep-red electroluminescentpolymers: synthesis and characterization of new low-band-gap conjugatedcopolymers for light-emitting diodes and photovoltaic devices. Macromolecules, 2005, 38: 244–253.
doi:10.1021/ma047969i
|
| 10 |
Hou Q, Niu Y H, Yang W, Yang R Q, Yuan M, Cao Y . Synthesisand electroluminescent properties of copolymer of fluorene and thiophene. Acta Polymerica Sinica, 2003, 2: 161–166 (in Chinese)
|
| 11 |
Schulze K, Uhrich C, Schüppel R, Leo K, Pfeiffer M, Brier E, Reinold E, Bäuerle P . Efficient vacuum-deposited organic solar cells basedon a new low-bandgap oligothiophene and fullerene C-60. Adv Mater, 2006, 18: 2872–2875.
doi:10.1002/adma.200600658
|
| 12 |
Padinger F, Rittberger R S, Sariciftci N S . Effects of postproduction treatment on plastic solarcells. Adv Funct Mater, 2003, 13: 85–88.
doi:10.1002/adfm.200390011
|
| 13 |
Ma W L, Yang C Y, Gong X, Lee K, Heeger A J . Thermally stable, efficient polymer solarcells with nanoscale control of the interpenetrating network morphology. Adv Funct Mater, 2005, 15: 1617–1622.
doi:10.1002/adfm.200500211
|
| 14 |
Li G, Shrotriya V, Huang J S, Yao Y, Moriarty T, Emery K, Yang Y . High-efficiency solutionprocessable polymer photovoltaic cells by self-organization of polymerblends. Nat Mater, 2005, 4: 864–868.
doi:10.1038/nmat1500
|
| 15 |
Wang W L, Wu H B, Yang C Y, Luo C, Zhang Y, Chen J W, Cao Y . High-efficiency polymer photovoltaicdevices from regioregular-poly(3-hexylthiophene-2,5-diyl) and [6,6]-phenyl-C-61-butyricacid methyl ester processed with oleic acid surfactant. Appl Phys Lett, 2007, 90: 183512-1–183512-3
|
| 16 |
Zhang F L, Perzon E, Wang X J, Mammo W, Andersson M R, Inganäs O . Polymer solar cells based on a low-bandgap fluorene copolymerand a fullerene derivative with photocurrent extended to 850 nm. Adv Funct Mater, 2005, 15: 745–750.
doi:10.1002/adfm.200400416
|
| 17 |
Sun M L, Niu Q L, Du B, Peng J B, Yang W, Cao Y . Fluorene-basedsingle-chain copolymers for color-stable white light-emitting diodes. Macromol Chem Phys, 2007, 208: 988–993.
doi:10.1002/macp.200700016
|
| 18 |
Li Y F, Cao Y, Gao J, Wang D L, Yu G, Heeger A J . Electrochemicalproperties of luminescent polymers and polymer light-emitting electrochemicalcells. Synth Met, 1999, 99: 243–248.
doi:10.1016/S0379‐6779(99)00007‐7
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|