State Environmental Protection Key Laboratory of Integrated Surface Water-Groundwater Pollution Control, School of Environmental Science and Engineering, Southern University of Science and Technology, Shenzhen 518055, China
• Cu and Cr can be mostly incorporated into CuFexAlyCr2−x−yO4 with a spinel structure.
• Spinel phase is the most crucial structure for Cu and Cr co-stabilization.
• Compared to Al, Fe and Cr are easier to be incorporated into the spinel structure.
• ‘Waste-to-resource’ by thermal process at attainable temperatures can be achieved.
Chromium slag usually contains various heavy metals, making its safe treatment difficult. Glass-ceramic sintering has been applied to resolve this issue and emerged as an effective method for metal immobilization by incorporating heavy metals into stable crystal structures. Currently, there is limited knowledge about the reaction pathways adopted by multiple heavy metals and the co-stabilization functions of the crystal structure. To study the Cu/Cr co-stabilization mechanisms during thermal treatment, a simulated system was prepared using a mixture with a molar ratio of Al2O3:Fe2O3:Cr2O3:CuO= 1:1:1:3. The samples were sintered at temperatures 600–1300°C followed by intensive analysis of phase constitutions and microstructure development. A spinel phase (CuFexAlyCr2−x−yO4) started to generate at 700°C and the incorporation of Cu/Cr into the spinel largely complete at 900°C, although the spinel peak intensity continued increasing slightly at temperatures above 900°C. Fe2O3/Cr2O3 was more easily incorporated into the spinel at lower temperatures, while more Al2O3 was gradually incorporated into the spinel at higher temperatures. Additionally, sintered sample microstructures became more condensed and smoother with increased sintering temperature. Cu / Cr leachability substantially decreased after Cu/Cr incorporation into the spinel phase at elevated temperatures. At 600°C, the leached ratios for Cu and Cr were 6.28% and 0.65%, respectively. When sintering temperature was increased to 1300°C, the leached ratios for all metal components in the system were below 0.2%. This study proposes a sustainable method for managing Cu/Cr co-exist slag at reasonable temperatures.
S Ballesteros, J M Rincón, B Rincón-Mora, M M Jordán (2017). Vitrification of urban soil contamination by hexavalent chromium. Journal of Geochemical Exploration, 174: 132–139 https://doi.org/10.1016/j.gexplo.2016.07.011
2
W H Bragg, W L Bragg (1913). The reflection of X-rays by crystals. Proceedings of the Royal Society of London. Series A, Containing Papers of a Mathematical and Physical Character, 88(605): 428–438 https://doi.org/10.1098/rspa.1913.0040
3
M E Brown, P K Gallagher (2011). Handbook of Thermal Analysis and Calorimetry: Recent Advances, Techniques and Applications. Amsterdam: Elsevier Science
4
A A V Cerbo, F Ballesteros Jr, T C Chen, M C Lu (2017). Solidification/stabilization of fly ash from city refuse incinerator facility and heavy metal sludge with cement additives. Environmental Science and Pollution Research International, 24(2): 1748–1756 https://doi.org/10.1007/s11356-016-7943-z
5
Q Chen, L Zhang, Y Ke, C Hills, Y Kang (2009). Influence of carbonation on the acid neutralization capacity of cements and cement-solidified/stabilized electroplating sludge. Chemosphere, 74(6): 758–764 https://doi.org/10.1016/j.chemosphere.2008.10.044
6
G A El-Shobaky, G A Fagal, N H Amin (1989). Thermal solid-solid interaction between CuO and pure Al2O3 solids. Thermochimica Acta, 141: 205–216 https://doi.org/10.1016/0040-6031(89)87055-8
7
F Fu, L Xie, B Tang, Q Wang, S Jiang (2012). Application of a novel strategy—Advanced fenton-chemical precipitation to the treatment of strong stability chelated heavy metal containing wastewater. Chemical Engineering Journal, 189–190: 283–287 https://doi.org/10.1016/j.cej.2012.02.073
8
J H Kim, J S Kim, S H Han, H W Kang, H G Lee, C I Cheon (2017). Low-temperature sintering and piezoelectric properties of CuO-doped (K,Na)NbO3 ceramics. Materials Research Bulletin, 96: 121–125 https://doi.org/10.1016/j.materresbull.2017.03.066
9
C Liao, Y Tang, C Liu, K Shih, F Li (2016). Double-Barrier mechanism for chromium immobilization: A quantitative study of crystallization and leachability. Journal of Hazardous Materials, 311: 246–253 https://doi.org/10.1016/j.jhazmat.2016.03.020
10
G Ma, A Garbers-Craig (2006). A review on the characteristics, formation mechanisms and treatment processes of Cr (VI)-containing pyrometallurgical wastes. Journal of the Southern African Institute of Mining and Metallurgy, 106: 753–763
11
W Ma, F Meng, D Qiu, Y Tang (2020). Co-stabilization of Pb/Cu/Zn by beneficial utilization of sewage sludge incineration ash: Effects of heavy metal type and content. Resources, Conservation and Recycling, 156: 104671 https://doi.org/10.1016/j.resconrec.2019.104671
12
L Mao, R Tang, Y Wang, Y Guo, P Su, W Zhang (2018). Stabilization of electroplating sludge with iron sludge by thermal treatment via incorporating heavy metals into spinel phase. Journal of Cleaner Production, 187: 616–624 https://doi.org/10.1016/j.jclepro.2018.03.235
13
G M Naja, B Volesky (2009). Treatment of metal-bearing effluents: Removal and recovery. Heavy Metals in the Environment, 247–292
14
N Okuno, Y Ishikawa, A Shimizu, M Yoshida (2004). Utilization of sludge in building material. Water science and technology: A journal of the International Association on Water Pollution Research, 49: 225–232
15
S OuYang, Y Zhang, Y Chen, Z Zhao, M Wen, B Li, Y Shi, M Zhang, S Liu (2019). Preparation of glass-ceramics using chromium-containing stainless steel slag: Crystal structure and solidification of heavy metal chromium. Scientific Reports, 9(1): 1964-1973 https://doi.org/10.1038/s41598-018-37996-4
16
Y Qu, Y Yang, Z Zou, C Zeilstra, K Meijer, R Boom (2014). Thermal decomposition behaviour of fine iron ore particles. ISIJ International, 54(10): 2196–2205 https://doi.org/10.2355/isijinternational.54.2196
17
J G Roessler, W N Oehmig, N I Blaisi, T G Townsend (2014). Chemical characterization of high-temperature arc gasification slag with a focus on element release in the environment. Environmental Science & Technology, 48(14): 7781–7788 https://doi.org/10.1021/es5007803
18
Y Sarıkaya, K Ada, M Önal (2008). A model for initial-stage sintering thermodynamics of an alumina powder. Powder Technology, 188(1): 9–12 https://doi.org/10.1016/j.powtec.2008.03.005
19
K Shih, Y Tang (2011). Prolonged toxicity characteristic leaching procedure for nickel and copper aluminates. Journal of Environmental Monitoring, 13(4): 829–835 https://doi.org/10.1039/c0em00596g
20
K Shih, Y Tang (2012). Incorporating simulated zinc ash by kaolinite- and sludge-based ceramics: Phase transformation and product leachability. Chinese Journal of Chemical Engineering, 20(3): 411–416 https://doi.org/10.1016/S1004-9541(11)60147-X
21
W Stumm, J J Morgan (2013). Aquatic Chemistry: Chemical Equilibria and Rates in Natural Waters. London: Wiley Blackwell
22
Y Tang, S W Chan, K Shih (2014a). Copper stabilization in beneficial use of waterworks sludge and copper-laden electroplating sludge for ceramic materials. Waste Management (New York, N.Y.), 34(6): 1085–1091 https://doi.org/10.1016/j.wasman.2013.07.001
23
Y Tang, S S Y Chui, K Shih, L Zhang (2011). Copper stabilization via spinel formation during the sintering of simulated copper-laden sludge with aluminum-rich ceramic precursors. Environmental Science & Technology, 45(8): 3598–3604 https://doi.org/10.1021/es103596k
24
Y Tang, X Lu, K Shih (2014b). Alumina polymorphs affect the metal immobilization effect when beneficially using copper-bearing industrial sludge for ceramics. Chemosphere, 117: 575–581 https://doi.org/10.1016/j.chemosphere.2014.08.065
25
Y Tang, K Shih, K Chan (2010). Copper aluminate spinel in the stabilization and detoxification of simulated copper-laden sludge. Chemosphere, 80(4): 375–380 https://doi.org/10.1016/j.chemosphere.2010.04.048
26
Y Tang, K Shih, C Liu, C Liao (2016). Cubic and tetragonal ferrite crystal structures for copper ion immobilization in an iron-rich ceramic matrix. RSC Advances, 6(34): 28579–28585 https://doi.org/10.1039/C6RA00168H
27
T Tsuchida, R Furuichi, T Sukegawa, M Furudate, T Ishii (1984). Thermoanalytical study on the reaction of the CuO—Al2O3(h, g AND α) systems. Thermochimica Acta, 78(1-3): 71–80 https://doi.org/10.1016/0040-6031(84)87134-8
28
F Wu, Y Tang, X Lu, C Liu, Y Lv, H Tong, Z Ning, C Liao, F Li (2019). Simultaneous immobilization of Zn(II) and Cr(III) in spinel crystals from beneficial utilization of waste brownfield-site soils. Clays and Clay Minerals, 67(4): 315–324 https://doi.org/10.1007/s42860-019-00053-w
29
P Wu, Y Tang, Z Cai (2018). Dual role of coal fly ash in copper ion adsorption followed by thermal stabilization in a spinel solid solution. RSC Advances, 8(16): 8805–8812 https://doi.org/10.1039/C7RA11495H