Coatings of needle/stripe-like fluoridated hydroxyapatite on H2O2-treated carbon/carbon composites prepared by induction heating and hydrothermal methods
Coatings of needle/stripe-like fluoridated hydroxyapatite on H2O2-treated carbon/carbon composites prepared by induction heating and hydrothermal methods
1. Shenzhen Key Laboratory of Special Functional Materials, Department of Materials Science and Engineering, Shenzhen University, Shenzhen 518060, China; 2. Key Laboratory of Auxiliary Chemical & Technology for Chemical Industry (Ministry of Education), Shaanxi University of Science and Technology, Xi’an 710021, China
A hydroxyapatite (HA) coating was achieved on H2O2-treated carbon/carbon (C/C) composite through hydrothermally treating and induction heating deposited CaHPO4 coating in an ammonia solution under ultrasonic water bath. Then, this HA coating was placed in a NH4F solution and hydrothermally treated again to fabricate fluorinated hydroxyapatite (FHA) coatings for 24 h at 353, 373, 393 and 413 K, respectively. The structure, morphology and chemical composition of the HA and FHA coatings were characterized by SEM, XRD, EDS and FTIR, and the adhesiveness and chemical stability of these FHA coatings were examined by a scratch test and an immersion test, respectively. The results showed that the as-prepared FHA coatings contained needle-like or stripe-like crystals, different from those of the HA coating. As the fluoridation temperature rose, the adhesiveness of the FHA coating first increased from 34.8 to 40.9 N at a temperature between 353 and 393 K, and then decreased to 24.2 N at 413 K, while the dissolution rate of the FHA coating decreased steadily. The reasons for the property variation of the FHA coatings were proposed by analyzing the morphology, composition and structure of the coatings.
Zhao X N, Hu T, Li H J, . Electrochemically assisted codeposition of calcium phosphate/collagen coatings on carbon/carbon composites. Applied Surface Science , 2011, 257(8): 3612–3619
2
Cao N, Dong J W, Wang Q X, . Plasma-sprayed hydroxyapatite coating on carbon/carbon composite scaffolds for bone tissue engineering and related tests in vivo. Journal of Biomedical Materials Research Part A , 2010, 92(3): 1019–1027
3
Huang J F, Zhu G Y, Cao L Y, . Influence of deposition voltage on phases and microstructure of hydroxyapatite coatings prepared on C-C composites by hydrothermal electrodeposition. Materials Technology: Advanced Performance Materials , 2007, 22(2): 88–90
4
Zhai Y Q, Li K Z, Li H J, . Influence of NaF concentration on fluorine-containing hydroxyapatite coating on carbon/carbon composites. Materials Chemistry and Physics , 2007, 106(1): 22–26
5
Cheng K, Ren C, Weng W, . Bonding strength of fluoridated hydroxyapatite coatings: a comparative study on pull-out and scratch analysis. Thin Solid Films , 2009, 517(17): 5361–5364
6
Zhang S, Zeng X T, Wang Y S, . Adhesion strength of sol–gel derived fluoridated hydroxyapatite coatings. Surface and Coatings Technology , 2006, 200(22-23): 6350–6354
7
Kim H W, Kim H E, Knowles J C. Fluor-hydroxyapatite sol–gel coating on titanium substrate for hard tissue implants. Biomaterials , 2004, 25(17): 3351–3358
8
Wang J, Chao Y L, Wan Q B, . Fluoridated hydroxyapatite coatings on titanium obtained by electrochemical deposition. Acta Biomaterialia , 2009, 5(5): 1798–1807
9
Lee E J, Lee S H, Kim H W, . Fluoridated apatite coatings on titanium obtained by electron-beam deposition. Biomaterials , 2005, 26(18): 3843–3851
10
Wang C, Li K-Z, Zhai Y-Q, . Study of fluorhydroxyapatite coatings on carbon/carbon composites. Surface and Coatings Technology , 2009, 203(13): 1771–1775
11
Xiong X-B, Liao B-C, Huang J-F, . Conversion of HA on NT-C/C composites from ultrasonic induction heating deposited monetite to FHA coating by an alkaline followed by NaF solution hydrothermal treatment methods. Journal of Inorganic and Organometallic Polymers and Materials , 2011, 21(3): 431–437
12
Xiong X-B, Zeng X-R, Zhou C-L. Preparation of enhanced HA coating on H2O2-treated carbon/carbon composite by induction heating and hydrothermal treatment methods. Materials Chemistry and Physics , 2009, 114(1): 434–438
13
Xiong X-B, Chu C-C, Huang J-F, . Preparation and characterization of fluoridated hydroxyapatite coatings on HT-C/C composites. Surface and Coatings Technology , 2012, 206(8-9): 2535–2540
14
Bogdanoviciene I, Beganskiene A, T?nsuaadu K, . Calcium hydroxyapatite, Ca10(PO4)6(OH)2 ceramics prepared by aqueous sol–gel processing. Materials Research Bulletin , 2006, 41(9): 1754–1762
16
Xu G F, Aksay I A, Groves J T. Continuous crystalline carbonate apatite thin films. A biomimetic approach. Journal of the American Chemical Society , 2001, 123(10): 2196–2203
17
De Maeyer E A, Verbeeck R M H, Pieters I Y. Effect of K+ on the stoichiometry of carbonated hydroxyapatite obtained by the hydrolysis of monetite. Inorganic Chemistry , 1996, 35(4): 857–863
18
Eslami H, Solati-Hashjin M, Tahriri M. The comparison of powder characteristics and physicochemical, mechanical and biological properties between nanostructure ceramics of hydroxyapatite and fluoridated hydroxyapatite. Materials Science and Engineering C , 2009, 29(4): 1387–1398
19
Xiong X B, Zeng X R, Zou C L. Bioactive calcium phosphate coating on carbon/carbon composites prepared by ultrasonicated induction heating deposition. Advanced Materials Research , 2011, 152-153: 1763–1766
20
Kozerski S, Pawlowski L, Jaworski R, . Two zones microstructure of suspension plasma sprayed hydroxyapatite coatings. Surface and Coatings Technology , 2010, 204(9-10): 1380–1387
21
Zhai Y Q, Li K Z, Li H J, . A fluorine-containing hydroxyapatite bioactive coating on the surface of C/C composites. Chinese Journal of Materials Research , 2007, 21(6): 570–576 (in Chinese)