Permeability and thermal conductivity test units were set up to study the heat and mass transfer performance of the host material, i.e. expanded natural graphite (ENG), for consolidated activated carbon (AC) adsorbent. The permeability was tested with nitrogen as the gas source, and the thermal conductivity was studied using steady-state heat source method. The results showed that the values of permeability and thermal conductivity were 10-15 to 10-12 m2 and 1.7 to 3.2 W/(m·K), respectively, while the density compressed expanded natural graphite (CENG) varied from 100 to 500 kg/m3. The permeability decreased with the increasing density of CENG, whereas the thermal conductivity increased with the increasing density of CENG. Then the thermal conductivity and permeability of granular AC were researched. It was discovered that the thermal conductivity of samples with different grain size almost kept constant at 0.36 W/(m·K) while the density was approximately 600 kg/m3. This means that the thermal conductivity was not related to the grain size of AC. The thermal conductivity of CENG was improved by 5 to 10 times compared with that of granular AC. Such a result showed that CENG was a promising host material for AC to improve the heat transfer performance, while the mass transfer performance should be considered in different conditions for utilization of adsorbent.
Mauran S, Lebrun M, Prades P, Moreau M, Spinner B, Drapier C. Active composite and its use as reaction medium. US Patent 5283219, 1994
2
Mauran S, Coudevylle O, Lu H B. Optimization of porous reactive media for solid sorption heat pumps. In: Proceedings of the International Sorption Heat Pump Conference, Montreal, Canada , 1996, 3–8
3
Klein H-P, Groll M. Heat transfer characteristics of expanded graphite matrices in metal hydride beds. International Journal of Hydrogen Energy , 2004, 29(14): 1503–1511 doi: 10.1016/j.ijhydene.2004.01.017
4
Menard D, Py X, Mazet N. Activated carbon monolith of high thermal conductivity for adsorption processes improvement, Part A: Adsorption step. Chemical Engineering and Processing , 2005, 44(9): 1029–1038 doi: 10.1016/j.cep.2005.02.002
5
Ahmet S, Ali K. Thermal conductivity and latent heat thermal energy storage characteristics of paraffin/expanded graphite composite as phase change material. Applied Thermal Engineering , 2007, 27(8,9): 1271–1277
6
Han J H, Lee K H. Gas permeability of expanded graphite-metallic salt composite. Applied Thermal Engineering , 2001, 21(4): 453–463 doi: 10.1016/S1359-4311(00)00056-9
7
Biloe S, Mauran S. Gas flow through highly porous graphite matrices. Carbon , 2003, 41(3): 525–537 doi: 10.1016/S0008-6223(02)00363-9
8
Lisker I S, Solovyev S V, Axcell B P, Varlow B R, Donnelly K.A transient technique for measuring the thermal conductivity of non-metals. Experimental Thermal and Fluid Science , 2001, 25(6): 377–382
9
Hirata K F Y, Fujioka K, Fujiki S. Preparation of fine particles of calcium chloride with expanded graphite for enhancement of the driving reaction for chemical heat pumps. Journal of Chemical Engineering of Japan , 2003, 36(7): 827–832 doi: 10.1252/jcej.36.827
10
Solórzano E, Reglero J A, Rodríguez-Pérez M A, Lehmhus D, Wichmann M, de Saja J A.An experimental study on the thermal conductivity of aluminium foams by using the transient plane source method. International Journal of Heat and Mass Transfer , 2008, 51(25,26): 6259–6267
11
Wang K, Wu J Y, Wang R, Wang L. Effective thermal conductivity of expanded graphite–CaCl2 composite adsorbent for chemical adsorption chillers. Energy Conversion and Management , 2006, 47(13,14): 1902–1912 doi: 10.1016/j.enconman.2005.09.005
12
Wang L W, Tamainot-Telto Z, Metcalf S J, Critoph R E, Wang R Z. Anisotropic thermal conductivity and permeability of compacted expanded natural graphite. Applied Thermal Engineering , 2010, 30(13): 1805–1811 doi: 10.1016/j.applthermaleng.2010.04.014
13
Tamainot-Telto Z, Critoph R E. Monolithic carbon for sorption refrigeration and heat pump applications. Applied Thermal Engineering , 2001, 21(1): 37–52 doi: 10.1016/S1359-4311(00)00030-2