Portevin-Le Chatelier effect of LA41 magnesium alloys
Portevin-Le Chatelier effect of LA41 magnesium alloys
WANG Cong1, WANG Cong1, HAN Enhou1, HAN Enhou1, XU Yongbo2, XU Yongbo2
1.Environmental Corrosion Center, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China; 2.Shenyang National Laboratory for Material Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China;
Abstract：Uni-axial tensile deformation of LA41 magnesium alloy has been carried out and the Portevin-Le Chatelier (PLC) effect, also known as serrated flow or plastic instability, is observed. This kind of alloy exhibits negative strain rate sensitivity (SRS) at room temperature, that is, SRS is negative at the strain rate range from 3.33?10-4 to 6.66?10-3 s-1 at ambient temperature. Both ultimate stress (?b) and 0.2% proof stress (?0.2) decrease when strain rate (ε°) increases, whilst critical strain (εc) of serrated flow is found to rise with enhancing ε°. A new explanation for this unusual phenomenon is presented. The model of dynamic strain aging (DSA) is established through diffusion of solute atoms to mobile dislocations, which are temporarily arrested at obstacles. Such interaction renders the movement of mobile dislocations more difficult so as to necessitate the required force to overcome the obstacles.
出版日期: 2007-03-05
引用本文:
. Portevin-Le Chatelier effect of LA41 magnesium alloys[J]. Frontiers of Materials Science in China, 2007, 1(1): 105-108.
WANG Cong, WANG Cong, HAN Enhou, HAN Enhou, XU Yongbo, XU Yongbo. Portevin-Le Chatelier effect of LA41 magnesium alloys. Front. Mater. Sci., 2007, 1(1): 105-108.