Abstract：In this paper, a novel combination method of electrospinning and rapid prototyping (RP) fused deposition modeling (FDM) is proposed for the fabrication of a tissue engineering heart valve (TEHV) scaffold. The scaffold preparation consisted of two steps: tri-leaflet scaffold fabrication and heart valve ring fabrication. With the purpose of mimicking the anisotropic mechanical properties of the natural heart valve leaflet, electrospun thermoplastic polyurethane (ES-TPU) was introduced as the tri-leaflet scaffold material. ES-TPU scaffolds can be fabricated to have a well-aligned fiber network, which is important for applications involving mechanically anisotropic soft tissues. We developed ES-TPU scaffolds as heart valve leaflet materials under variable speed conditions and measured fiber alignment by fast Fourier transform (FFT). By using FFT to assign relative alignment values to an electrospun matrix, it is possible to systematically evaluate how different processing variables affect the structure and material properties of a scaffold. TPU was suspended at certain concentrations and electrospun from 1,1,1,3,3,3-hexafluoro-2-propanol onto rotating mandrels (200―3000 rpm). The scaffold morphological property and mechanical anisotropic property are discussed in the paper as a function of fiber diameter and mandrel RPM. The induction of varying degrees of anisotropy imparted distinctive material properties to the electrospun scaffolds. A dynamic optimum design of the heart valve ring graft was constructed by FDM. Fabrication of a 3D heart valve ring was constructed using pro-engineer based on optimum hemodynamic analysis and was converted to an STL file format. The model was then created from PCL which was sewed and glued with electrospun nanofibrous leaflets. This proposed method was proven as a promising fabrication process in fabricating a specially designed graft with the correct physical and mechanical properties.
Brody S, Pandit A. Approaches to heart valvetissue engineering scaffold design. Journalof Biomedical Materials Research - Part B Applied Biomaterials, 2007, 83(1): 16–43 doi: 10.1002/jbm.b.30763
Rosamond W, Flegal K, Furie K, et al. Heart disease and stroke statistics ―2008 update: a report from the American Heart Association StatisticsCommittee and Stroke Statistics Subcommittee. Circulation, 2008, 117(4)
Kidane A G, Burriesci G, Cornejo P, et al. Current developments and future prospects forheart valve replacement therapy. Journalof Biomedical Materials Research - Part B Applied Biomaterials, 2009, 88(1): 290–303 doi: 10.1002/jbm.b.31151
Weinand C, Pomerantseva I, Neville C M, et al. Hydrogel-beta-TCP scaffolds and stem cells fortissue engineering bone. Bone, 2006, 38(4): 555–563 doi: 10.1016/j.bone.2005.10.016
Takagi K, Fukunaga S, Nishi A, et al. In vivo recellularizationof plain decellularized xenografts with specific cell characterizationin the systemic circulation: Histological and immunohistochemicalstudy. Artificial Organs, 2006, 30(4): 233–241 doi: 10.1111/j.1525-1594.2006.00210.x
Martina M, Subramanyam G, Weaver J C, et al. Developing macroporous bicontinuous materialsas scaffolds for tissue engineering. Biomaterials, 2005, 26(28): 5609–5616 doi: 10.1016/j.biomaterials.2005.02.011
Masood S H, Singh J P, Morsi Y. The design and manufacturing of porous scaffolds fortissue engineering using rapid prototyping. International Journal of Advanced Manufacturing Technology, 2005, 27(3―4): 415–420 doi: 10.1007/s00170-004-2187-3
Landers R, Hübner U, Schmelzeisen R, et al. Rapid prototyping of scaffolds derived fromthermoreversible hydrogels and tailored for applications in tissueengineering. Biomaterials, 2002, 23(23): 4437–4447 doi: 10.1016/S0142-9612(02)00139-4
Landers R, Pfister A, Huübner U, et al. Fabrication of soft tissue engineering scaffoldsby means of rapid prototyping techniques. Journal of Materials Science, 2002, 37(15): 3107–3116 doi: 10.1023/A:1016189724389
Zong X H, Kim K, Fang D F, et al. Structure and process relationship of electrospunbioabsorbable nanofiber membranes. Polymer, 2002, 43(16): 4403–4412 doi: 10.1016/S0032-3861(02)00275-6
Webster T J, Waid M C, McKenzie J L, et al. Nano-biotechnology: carbon nanofibres as improvedneural and orthopaedic implants. Nanotechnology, 2004, 15(1): 48–54 doi: 10.1088/0957-4484/15/1/009
Pedicini A, Farris R J. Mechanical behavior of electrospunpolyurethane. Polymer, 2003, 44(22): 6857–6862 doi: 10.1016/j.polymer.2003.08.040
Tatai L, Moore T G, Adhikari R, et al. Thermoplastic biodegradable polyurethanes: Theeffect of chain extender structure on properties and in-vitro degradation. Biomaterials, 2007, 28: 5407–5417 doi: 10.1016/j.biomaterials.2007.08.035
Huang Z M, Zhang Y Z, Ramakrishna S, et al. Electrospinning and mechanical characterizationof gelatin nanofibers. Polymer, 2004, 45(15): 5361–5368 doi: 10.1016/j.polymer.2004.04.005