Abstract：The mechanical property of prestressing steel wire during and after heating is the key factor in the design of fire resistance and after-fire damage evaluation of prestressed structures. Tensile experiment of 16 prestressing steel wires ( fptk = 1770 N/mm2, d = 5 mm, low relaxation of stress) at high temperature and tensile experiment of 14 prestressed steel wires after heating are carried out. According to the experiment, the shapes of stress-strain curves of steel wire at high temperature go smooth and the mechanical property indexes of the steel wire such as strength, modulus of elasticity, etc., degenerate continuously as temperature increased. According to the experiment after heating, the mechanical property of steel wire varies little when the highest temperature that the steel wire has ever been heated to is lower than 300vH; while the stress-strain curves of steel wire become more ductile and the mechanical property indexes of the steel wire degenerate gradually when the highest temperature is higher than 300vH. By applying the theory of viscoelastic mechanics, stress-strain curves of steel wire at high temperatures without loading rate influence are obtained. The law of mechanical property indexes of the wire is presented. The mathematical models of the stress-strain relationship of the pre-stressed steel wire are established. All can serve as basic data for the analysis of fire resistance and after-fire damage evaluation of pre-stressed structures.
出版日期: 2007-06-05
引用本文:
. Experimental research on the mechanical property of prestressing steel wire during and after heating[J]. Frontiers of Architecture and Civil Engineering in China, 2007, 1(2): 247-254.
ZHENG Wenzhong, HU Qiong, ZHANG Haoyu. Experimental research on the mechanical property of prestressing steel wire during and after heating. Front. Struct. Civ. Eng., 2007, 1(2): 247-254.