This study reports on the effects of multilayer graphene oxide (MGO) on compressive strength, flexural strength, and microstructure of cement mortar. The cement mortar was prepared with type P. II. 52.5 Portland cement, standard sand, and MGO. Four mixes were prepared with inclusion of MGO (0%, 0.02%, 0.04%, and 0.06% by weight of cement). The testing result shows that the compressive of GO-cement mortar increased by 4.84%–13.42%, and the flexural strength increased by 4.37%–8.28% at 3 d. GO-cement mortar’s compressive strength and flexural strength at 7 d increased by 3.84%–12.08% and 2.54%–13.43%, respectively. MGO made little contribution to the increases of compressive strength and flexural strength of cement mortar at 28 d. The results of X-ray diffraction (XRD), scanning electron microscope (SEM), and nitrogen (N2) adsorption/desorption tests show that the types of hydration products and crystal grain size did not change after adding MGO. Still, it can help to improve the microstructure of the cement mortar via regulating hydration products and can provide more condensed cores to accelerate hydration. Furthermore, the regulating action of MGO for the microstructure of cement mortar at an early age was better than that at 28 d.
S Chuah, Z Pan, J G Sanjayan, C M Wang, W H Duan. Nano reinforced cement and concrete composites and new perspective from graphene oxide. Construction & Building Materials, 2014, 73: 113–124 https://doi.org/10.1016/j.conbuildmat.2014.09.040
2
Y G Hou, S H Lv, L P Liu, X Liu. High-quality preparation of graphene oxide via the Hummers’ method: Understanding the roles of the intercalator, oxidant, and graphite particle size. Ceramics International, 2020, 46(2): 2392–2402 https://doi.org/10.1016/j.ceramint.2019.09.231
3
S Sharma, N C Kothiyal. Influence of graphene oxide as dispersed phase in cement mortar matrix in defining the crystal patterns of cement hydrates and its effect on mechanical, microstructural and crystallization properties. RSC Advances, 2015, 5(65): 52642–52657 https://doi.org/10.1039/C5RA08078A
4
W G Li, X Y Li, S J Chen, Y M Liu, W H Duan, S P Shah. Effects of graphene oxide on early-age hydration and electrical resistivity of Portland cement paste. Construction & Building Materials, 2017, 136: 506–514 https://doi.org/10.1016/j.conbuildmat.2017.01.066
5
Z Y Lu, X Y Li, A Hanif, B M Chen, P Parthasarathy, J G Yu, Z J Li. Early-age interaction mechanism between the graphene oxide and cement hydrates. Construction & Building Materials, 2017, 152: 232–239 https://doi.org/10.1016/j.conbuildmat.2017.06.176
6
H B Yang, M Monasterio, H Z Cui, N X Han. Experimental study of the effects of graphene oxide on microstructure and properties of cement paste composite. Composites. Part A, Applied Science and Manufacturing, 2017, 102: 263–272 https://doi.org/10.1016/j.compositesa.2017.07.022
7
X Y Li, C Y Li, Y M Liu, S J Chen, C M Wang, J G Sanjayan, W H Duan. Improvement of mechanical properties by incorporating graphene oxide into cement mortar. Mechanics of Advanced Materials and Structures, 2018, 25(15–16): 1313–1322 https://doi.org/doi:/10.1080/15376494.2016.1218226
8
X Y Li, Y M Liu, W G Li, C Y Li, J G Sanjayan, W H Duan, Z J Li. Effects of graphene oxide agglomerates on workability, hydration, microstructure and compressive strength of cement paste. Construction and Building Materials, 2017, 145: 402–410 https://doi.org/10.1016/j.conbuildmat.2017.04.058
9
Z Pan, L He, L Qiu, A H Korayem, G Li, J W Zhu, F Collins, D Li, W H Duan, M C Wang. Mechanical properties and microstructure of a graphene oxide-cement composite. Cement and Concrete Composites, 2015, 58: 140–147 https://doi.org/10.1016/j.cemconcomp.2015.02.001
10
S H Lv, H Y Hu, J Zhang, Y Lei, L Sun, Y G Hou. Structure, performances, and formation mechanism of cement composites with large-scale regular microstructure by distributing uniformly few-layered graphene oxide in cement matrix. Structural Concrete, 2019, 20(1): 471–482 https://doi.org/10.1002/suco.201800078
11
H Peng, Y P Ge, C S Cai, Y X Zhang, Z Liu. Mechanical properties and microstructure of graphene oxide cement-based composites. Construction & Building Materials, 2019, 194: 102–109 https://doi.org/10.1016/j.conbuildmat.2018.10.234
12
Q Wang, J Wang, C X Lu, B W Liu, K Zhang, C Z Li. Influence of graphene oxide additions on the microstructure and mechanical strength of cement. New Carbon Materials, 2015, 30(4): 349–356 https://doi.org/10.1016/S1872-5805(15)60194-9
13
A Kudžma, J Škamat, R Stonys, A Krasnikovs, D Kuznetsov, G Girskas, V Antonovič. Study on the effect of graphene oxide with low oxygen content on Portland cement based composites. Materials. Materials (Basel), 2019, 12: 802 https://doi.org/10.3390/ma12050802
14
K Chintalapudi, R M R Pannem. The effects of Graphene Oxide addition on hydration process, crystal shapes, and microstructural transformation of ordinary Portland cement. Journal of Building Engineering, 2020, 32: 101551 https://doi.org/10.1016/j.jobe.2020.101551
15
M E Abrishami, V Zahabi. Reinforcing graphene oxide/cement composite with NH2 functionalizing group. Bulletin of Materials Science, 2016, 39(4): 1073–1078 https://doi.org/10.1007/s12034-016-1250-7
16
L Zhao, X L Guo, C Ge, Q Li, X Shu, L P Guo, X Shu, J P Liu. Mechanical behavior and toughening mechanism of polycarboxylate superplasticizer modified graphene oxide reinforced cement composites. Composites Part B: Engineering, 2017, 113: 308–316 https://doi.org/10.1016/j.compositesb.2017.01.056
17
K Gong, Z Pan, A H Korayem, L Qiu. Reinforcing effects of graphene oxide on Portland cement paste. Journal of Materials in Civil Engineering, 2014, 27(2): A4014010 https://doi.org/10.1061/(ASCE)MT.1943-5533.0001125
18
W G Li, X Y Li, S J Chen, G C Long, Y M Liu, W H Duan. Effects of nanoalumina and graphene oxide on early-age hydration and mechanical properties of cement paste. Journal of Materials in Civil Engineering, 2017, 29(9): 04017087 https://doi.org/10.1061/(ASCE)MT.1943-5533.0001926
19
J C Pang, Y M Wang. Graphene oxide on the microstructure and mechanical properties of cement based composite material. Fracture and Structural Integrity, 2018, 45: 156–163 https://doi.org/10.3221/IGF-ESIS.45.13
20
S J Lee, S H Jeong, D U Kim, J P Won. Effects of graphene oxide on pore structure and mechanical properties of cementitious composites. Composite Structures, 2020, 234: 111709 https://doi.org/10.1016/j.compstruct.2019.111709
21
W J Long, J J Wei, F Xing, K H Khayat. Enhanced dynamic mechanical properties of cement paste modified with graphene oxide nanosheets and its reinforcing mechanism. Cement and Concrete Composites, 2018, 93: 127–139 https://doi.org/10.1016/j.cemconcomp.2018.07.001
22
J Chen, Y R Li, L Huang, C Li, G Q Shi. High-yield preparation of graphene oxide from small graphite flakes via an improved Hummers method with a simple purification process. Carbon, 2015, 81: 826–834 https://doi.org/10.1016/j.carbon.2014.10.033
H J Yang, H Y Li, J L Zhai, L Sun, H W Yu. Simple synthesis of graphene oxide using ultrasonic cleaner from expanded graphite. Industrial & Engineering Chemistry Research, 2014, 53(46): 17878–17883 https://doi.org/10.1021/ie503586v
25
W J Lu, F X Qin, Q C Zhang, C Remillat, H Wang, F Scarpa, H X Peng. Engineering foam skeletons with multilayered graphene oxide coatings for enhanced energy dissipation. Composites. Part A, Applied Science and Manufacturing, 2020, 137: 106035 https://doi.org/10.1016/j.compositesa.2020.106035
26
C B Qin, Z X Qiao, W J He, Y N Gong, G F Zhang, R Y Chen, Y Gao, L T Xiao, S T Jia. Laser-driven propulsion of multilayer graphene oxide flakes. Journal of Materials Chemistry. C, Materials for Optical and Electronic Devices, 2018, 6(9): 2329–2335 https://doi.org/10.1039/C7TC05661C
Y Wei, Y S Zhang, X L Gao, Z Ma, X J Wang, C J Gao. Multilayered graphene oxide membranes for water treatment: A review. Carbon, 2018, 139: 964–981 https://doi.org/10.1016/j.carbon.2018.07.040
29
J Q Wang, P Zhang, B Liang, Y X Liu, T Xu, L F Wang, B Cao, K Pan. Graphene oxide as an effective barrier on a porous nanofibrous membrane for water treatment. ACS Applied Materials & Interfaces, 2016, 8(9): 6211–6218 https://doi.org/10.1021/acsami.5b12723
30
S Chiranjiakumari Devi, R Ahmad Khan. Influence of graphene oxide on sulfate attack and carbonation of concrete containing recycled concrete aggregate. Construction & Building Materials, 2020, 250: 118883 https://doi.org/10.1016/j.conbuildmat.2020.118883
31
Z S Chen, X Zhou, X Wang, P Guo. Mechanical behavior of multilayer GO carbon-fiber cement composites. Construction & Building Materials, 2018, 159: 205–212 https://doi.org/10.1016/j.conbuildmat.2017.10.094
32
GB/T 175–2007. Common Portland Cement. Chinese National Standard, 2007
33
JG/T 223–2007. Polycarboxylates High Performance Water-reducing Admixture. Chinese Construction Industry Standard, 2007
34
C Y Li, S J Chen, W G Li, X Y Li, D Ruan, W H Duan. Dynamic increased reinforcing effect of graphene oxide on cementitious nanocomposite. Construction & Building Materials, 2019, 206: 694–702 https://doi.org/10.1016/j.conbuildmat.2019.02.001
35
S H Lv, J J Liu, T Sun, Y J Ma, Q F Zhou. Effect of GO nanosheets on shapes of cement hydration crystals and their formation process. Construction & Building Materials, 2014, 64: 231–239 https://doi.org/10.1016/j.conbuildmat.2014.04.061
36
GB 17671–1999. Method of Testing Cements––Determination of strength. Chinese National Standard, 1999
37
GB/T 2419–2005. Test Method for Fluidity of Cement Mortar. Chinese National Standard, 2005
38
S Ghazizadeh, P Duffour, N T Skipper, Y Bai. Understanding the behaviour of graphene oxide in Portland cement paste. Cement and Concrete Research, 2018, 111: 169–182 https://doi.org/10.1016/j.cemconres.2018.05.016
39
L Wang, S Zhang, D Zheng, H Yang, H Cui, W Tang, D Li. Effect of graphene oxide (GO) on the morphology and microstructure of cement hydration products. Nanomaterials (Basel, Switzerland), 2017, 7(12): 429–439 https://doi.org/10.3390/nano7120429
40
X T Yan, D P Zheng, H B Yang, H Z Cui, M Monasterio, Y Lo. Study of optimizing graphene oxide dispersion and properties of the resulting cement mortars. Construction & Building Materials, 2020, 257: 119477 https://doi.org/10.1016/j.conbuildmat.2020.119477
41
G J Jing, J M Wu, T Y Lei, S X Wang, V Strokova, V Nelyubova, M J Wang, Z M Ye. From graphene oxide to reduced graphene oxide: Enhanced hydration and compressive strength of cement composites. Construction & Building Materials, 2020, 248: 118699 https://doi.org/10.1016/j.conbuildmat.2020.118699
42
J J Thomas, H M Jennings, J J Chen. Influence of nucleation seeding on the hydration mechanisms of tricalcium silicate and cement. Journal of Physical Chemistry C, 2009, 113(11): 4327–4334 https://doi.org/10.1021/jp809811w
43
P Mounanga, A Khelidj, A Loukili, V Baroghel-Bouny. Predicting Ca(OH)2 content and chemical shrinkage of hydrating cement pastes using analytical approach. Cement and Concrete Research, 2004, 34(2): 255–265 https://doi.org/10.1016/j.cemconres.2003.07.006
44
T S Qureshi, D K Panesar. Impact of graphene oxide and highly reduced graphene oxide on cement based composites. Construction & Building Materials, 2019, 206: 71–83 https://doi.org/10.1016/j.conbuildmat.2019.01.176
45
Q Wang, S Y Li, S Pan, X Y Cui, D J Corr, S P Shah. Effect of graphene oxide on the hydration and microstructure of fly ash-cement system. Construction & Building Materials, 2019, 198: 106–119 https://doi.org/10.1016/j.conbuildmat.2018.11.199
46
W J Long, H D Li, C L Fang, F Xing. Uniformly dispersed and re-agglomerated graphene oxide-based cement pastes: A comparison of rheological properties, mechanical properties and microstructure. Nanomaterials (Basel, Switzerland), 2018, 8(1): 31 https://doi.org/10.3390/nano8010031
47
X J Kang, X H Zhu, J S Qian, J P Liu, Y B Huang. Effect of graphene oxide (GO) on hydration of tricalcium silicate (C3S). Construction & Building Materials, 2019, 203: 514–524 https://doi.org/10.1016/j.conbuildmat.2019.01.117