Structure and performance of welding joint of
Q235 steel welded by SHS welding |
| Junzhi HU,Sumei WANG,Xiaoli ZHAO,Shilin ZHU,Botao YU, |
| China Power Complete
Equipment Co., Ltd., Beijing 100011, China; |
|
|
|
|
Abstract A self-propagating high-temperature synthesis (SHS) welding-pen that can weld steel workpiece from 6 to 10 mm is developed and welds the Q235 steel. The structure and properties of the welding joint are studied. The result indicates that this type of welding is melting and the fusion zone is clear. The tensile-strength of the welding joint is 283 MPa, flexural strength is 628 MPa, impact toughness is 46.43 J·cm−2, and the microhardness of the welding joint and fusion zone are 230 HV0.1 and 255.6€HV0.1, respectively. The mircohardness of the fusion zone and the welding line are higher than that of the matrix.
|
| Keywords
self-propagating high-temperature synthesis (SHS) welding
welding line
structure and performance
melting
|
|
Issue Date: 05 June 2010
|
|
|
Merzhanov A G. Self-propagating high-temperature synthesis: twenty yearsof search and findings. In: Combustion and Plasma Synthesis of High-TemperatureMaterials. New York, 1990, 1–53
|
|
Li S J. Joining of SiC ceramics to Ni-based superalloy with Cuintermediate layer. Key Engineering Materials, 2002, 27(3): 101–110
doi: 10.4028/www.scientific.net/KEM.217.101
|
|
Hu J Z, Ma S N, Chen X R. Structure and performance of a new cuprum-baseSHS welding material. Transactions of theChina Welding Institution, 2006, 27(10): 94–96 (in Chinese)
|
|
Hu J Z, Ma S N, Chen X R. Performance of welding joint on threeCu-base SHS welding materials. Transactions of Materials and Heat Treatment, 2007, 28(3): 81–84 (in Chinese)
|
|
Shi Y W. China Materials Engineering Ceremony (Vol.22): Welding Materials Engineering (I). Beijing: Chemical Industry Press, 2006 (in Chinese)
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|